Product having ultraviolet radiation protection

ABSTRACT

A product for incorporating ultraviolet radiation protection and antimicrobial protection into rayon is disclosed which has a quantity of rayon, a quantity of zinc oxide particles with each particle having a surface, and a quantity of a reactive group for modifying each surface of each zinc oxide particle, the quantity of the reactive group for incorporating the quantity of zinc oxide particles into the quantity of rayon prior to the quantity of rayon being formed into a fiber.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent applicationSer. No. 15/951,834 filed on Apr. 12, 2018, which was a continuation ofU.S. patent application Ser. No. 15/064,242 filed on Mar. 8, 2016, whichwas a continuation-in-part of U.S. patent application Ser. No.14/833,317 filed on Aug. 24, 2015, which is now U.S. Pat. No. 9,404,214,which was a continuation of U.S. patent application Ser. No. 14/245,152filed on Apr. 4, 2014, which is now U.S. Pat. No. 9,150,824, which was acontinuation of U.S. patent application Ser. No. 13/632,223 filed onOct. 1, 2012, which is now U.S. Pat. No. 8,690,964, which was acontinuation-in-part of U.S. patent application Ser. No. 13/317,152filed on Oct. 11, 2011, which is now U.S. Pat. No. 8,277,518.

BACKGROUND

This disclosure relates to an additive for incorporating ultravioletradiation (UV) protection into a polymer, and more specifically, to anadditive for incorporating UV protection and antimicrobial protectioninto rayon with the additive and the rayon for use in manufacturing asynthetic fabric, yarn, textile or garment.

Ecological friendly fabrics or Eco-friendly fabrics are gaining inpopularity and use in clothing. An Eco-friendly fabric may be a naturalfiber such as cotton, hemp, or bamboo which has been grown in soil thathas not been treated with pesticides for a number of years. Someexamples of other Eco-friendly fabrics are organic cotton, sisal, acombination of hemp and recycled rayon, a combination of hemp andcotton, broadcloth, denim, linen, and a combination of bamboo andrecycled rayon. Natural fibers, which may be derived from plants oranimals, such as wool, angora, silk, alpaca, cashmere, and silk are alsoexamples of Eco-friendly fabrics. Synthetic fabrics, which may be madefrom synthetic sustainable products, such as nylon, rayon, olefin,spandex, and tencel are also examples of Eco-friendly fabrics.

To assist an individual in determining whether a garment has protectionagainst ultraviolet radiation, a rating system has been developed. Thisrating system is known in the industry as the UPF (UltravioletProtection Factor) rating system. Clothing having a rating of UPF 50 areable to block out 98% of the sun's ultraviolet radiation. Further, byway of example, a garment having a rating of UPF 15-24 will only blockout 93.3% to 95.9% of ultraviolet radiation. Exposure to the sun'sharmful ultraviolet radiation (known as UVA/UVB rays) can damage theskin, can cause sunburn, and can lead to skin cancer over prolongedexposure.

There are a number of factors that affect the level of ultravioletradiation protection provided by a fabric and the UPF rating. Somefactors are the weave of the fabric, the color of the fabric, the weightof the fabric, the fiber composition of the fabric, the stretch of thefabric, moisture content of the fabric. If the fabric has a tight weaveor a high thread count then the fabric will have a higher UPF rating.However, even though the fabric has a higher UPF rating, the fabric maybe less comfortable because a tighter weave or higher thread count meansthat the fabric is heavy or uncomfortable to wear. Another factor thataffects protection is the addition of chemicals such as UV absorbers orUV diffusers during the manufacturing process. As can be appreciated,some of the features that make a garment comfortable to wear also makethe garment less protective. A challenge for a clothing manufacturer isto provide clothing having both protection from the sun and beingcomfortable to wear.

Athletic clothing or active wear clothing is typically manufactured fromsynthetic material such as polyester or nylon. Polyester may be formedinto a filament yarn that is used to weave a fabric or garment. To formpolyester, dimethyl terephthalate is placed in a container and firstreacted with ethylene glycol in the presence of a catalyst at atemperature of 302-410° F. The resulting chemical, a monomer alcohol, iscombined with terephthalic acid and raised to a temperature of 472° F.Newly-formed polyester, which is clear and molten, is extruded through aslot provided in the container to form long ribbons. the long moltenribbons are allowed to cool until they become brittle. The ribbons arecooled and then cut into tiny polymer chips. These tiny polymer chipsare then melted at 500-518° F. to form a syrup-like melt or liquid. Thismelt is put into a metal container called a spinneret and forced throughits tiny holes to produce special fibers. The emerging fibers arebrought together to form a single strand. This strand is wound on abobbin for further processing or to be woven into yarn.

Therefore, it would be desirable to provide an additive forincorporating ultraviolet radiation protection into a polymer prior to apolymer yarn being fabricated. Moreover, there is a need for a processfor incorporating UV protection into a polymer so that the polymer maybe further processed into a yarn that may be used to manufacture afabric so that the fabric may be used to protect an individual from UVradiation. Furthermore, it would be advantageous to incorporate adequateprotection in a garment, fabric, or textile to protect against exposureto UV radiation, to increase the UV resistance of a garment, fabric, ortextile, or to enhance UV radiation absorption of a garment, fabric, ortextile to protect an individual from UV radiation.

BRIEF SUMMARY

In one form of the present disclosure, a product having ultravioletradiation protection and antimicrobial protection is disclosed whichcomprises a quantity of rayon, a quantity of zinc oxide particles witheach particle having a surface, and a quantity of a reactive group formodifying each surface of each zinc oxide particle, the quantity of thereactive group for incorporating the quantity of zinc oxide particlesinto the quantity of rayon prior to the quantity of rayon being formedinto a fiber.

In another form of the present disclosure, a product for incorporatingultraviolet radiation protection and antimicrobial protection into rayonprior to the rayon being formed by use of a spinneret comprises aquantity of rayon, a quantity of zinc oxide particles, and a quantity ofa phosphoether of 4-hydroxybenzophenone.

In yet another form of the present disclosure, a product forincorporating ultraviolet radiation protection and antimicrobialprotection into rayon prior to forming rayon comprises a quantity ofrayon and a quantity of prepared zinc oxide particles modified with alayer of a reactive group that forms a bond with the quantity of rayonwith the quantity of prepared zinc oxide particles prepared bysuspending a quantity of zinc oxide particles in a solution of 98% ethylalcohol, suspending a quantity of benzophenone silane linker in thesolution of zinc oxide particles and 98% ethyl alcohol, adjusting the pHof the solution of zinc oxide particles, 98% ethyl alcohol, andbenzophenone silane linker to 12, placing the pH adjusted solution ofzinc oxide particles, 98% ethyl alcohol, and benzophenone silane linkerinto a centrifuge, recovering the zinc oxide particles prepared bycentrifugation after a period of time, and drying the recovered preparedzinc oxide particles for a period of time.

The present disclosure provides a product for incorporating ultravioletradiation protection and antimicrobial protection into rayon to be usedto produce or manufacture a fabric which is lightweight and can be wornin any temperature.

The present disclosure provides a product for incorporating ultravioletradiation protection and antimicrobial protection into rayon forproviding enhanced protection from both UVA and UVB radiation.

The present disclosure also provides a product for incorporatingultraviolet radiation protection and antimicrobial protection into rayonwhich retains ultraviolet radiation protection and antimicrobialprotection after use or after cleaning.

The present disclosure provides a product for incorporating ultravioletradiation protection and antimicrobial protection into rayon to be usedto produce or manufacture a fabric which is comfortable to wear.

The present disclosure provides a product for incorporating ultravioletradiation protection and antimicrobial protection into rayon which canbe incorporated into the production of rayon manufacturing.

The present disclosure also provides a product for incorporatingultraviolet radiation protection and antimicrobial protection into rayonwhich can be manufactured without increasing the cost of rayon.

The present disclosure provides a product for incorporating ultravioletradiation protection and antimicrobial protection into rayon that isincorporated into active wear clothing or athletic clothing.

The present disclosure is directed to an additive for incorporatingultraviolet radiation protection into a polymer, such as a syntheticpolymer, that is used to produce a synthetic yarn that is employed tomanufacture a fabric or garment.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

Various methods or processes are disclosed herein for the immobilizationof UV-blocking nanoparticles on Eco-friendly fabric to incorporate UVprotection in the fabric. Once the UV-blocking nanoparticles areattached, the Eco-friendly fabric will be able to protect a wearer ofthe fabric from UV radiation. One method comprises direct immobilizationfrom in situ formation of the particles. A second method comprisescarboxylation or phosphorylation of the fabric followed by binding ofthe UV-blocking nanoparticles to the modified fabric. A third methodcomprises modifying UV-blocking nanoparticles with a self-assembledmonolayer (SAM) or polymer layer containing an active chemical groupcapable of binding to the fabric and deposited on the fabric fromsolution.

ZnO (zinc oxide) nanoparticles are generally formed by the precipitationof a zinc salt (acetate, sulfate, nitrate, chloride) using eitheraqueous hydroxide or an amine. The following examples disclose directimmobilization from in situ formation of the ZnO nanoparticles.

Example 1 Solution Sol-Gel Process, Hydroxide Base

4.39 g. zinc acetate (20 mmol) is dissolved in 100 mL deionized ordistilled water. A textile is added to this solution and 100 mL 0.4MNaOH is added while mixing. The suspension is mixed for 2 hours to forma suspension of zinc oxide nanoparticles in contact with the fabric. Thetextile is removed from the nanoparticle suspension and laundered in ahousehold washing machine. As can be appreciated, a fabric may betreated to have ultraviolet radiation protection incorporated in thefabric by the steps of dissolving zinc acetate or other zinc salt in aliquid to form a solution containing Zn(II) ions, adding a fabric to thesolution, mixing the solution and the fabric, and adding a base to thesolution when the solution and the fabric are being mixed to form asuspension of zinc oxide nanoparticles in contact with the fabric.

Example 2 Solution Sol-Gel Process, Amine Base

4.39 g. zinc acetate (20 mmol) is dissolved in 100 mL deionized water. Atextile is added to this solution while mixing and 40 mmol amine isadded while mixing. Amines used may include ethanolamine,ethylenediamine, (tris)hydroxymethylaminomethane, or others. The textileis removed from the nanoparticle suspension and laundered in a householdwashing machine.

Example 3 Mechanochemical Process

5.75 g. zinc sulfate heptahydrate (20 mmol) and 0.88 g (15 mmol) sodiumchloride are powered finely and blended, then placed with a textile in aball mill or similar mechanical mixer. 1.6 g (40 mmol) sodium hydroxideis powdered and added to the mixer. After twenty minutes, the textile isremoved and rinsed thoroughly with water.

The following examples disclose carboxylation or phosphorylation of thefabric followed by binding of the UV-blocking nanoparticles to themodified fabric.

Example 4 Modification of Textile with Phosphonic Acid Groups

For this process it will be necessary to modify a textile withphosphonic acid groups. This can be accomplished in a number of ways,but it is desirable to use materials that are non-toxic and/or renewablysourced chemicals. Phosphorylated cellulose should form covalentlinkages with ZnO and TiO₂ nanoparticles. The interaction betweenphosphonates and oxide surfaces are used for modification of the oxidesurfaces. In essence, the procedure consists of condensing the cellulosetextile with a bis(phosphonic acid), phosphonate, or phosphate species,either organic or inorganic. Urea may be added to forestalldiscoloration of the textile. Phosphorylation takes place driven by theelimination of water. The resulting phosphorylated textile will directlybind both zinc oxide and titanium oxide nanoparticles. It will benecessary to restrict the degree of phosphorylation of the textile toprevent great alteration in the properties of the textile by controllinga reaction time. This process does not require in situ synthesis of thezinc oxide nanoparticles. Commercially available zinc oxidenanoparticles may be used.

A sample of cotton textile is wetted with a 10% v/v solution ofphosphoric acid or bis-phosphonic acid containing 10-30% w/v urea. Thetextile is pressed to remove excess solution and baked in an oven at85-100° C. for 5 minutes to dry, then at 170° C. for 2-4 minutes to cureunreacted groups. The textile is removed from the oven and washed withwater. The textile is then used without further modification insubsequent deposition steps.

Example 5 Modification of a Textile by Partial TEMPO-H₂O₂ Oxidation

A sample of cotton textile (ca. 1 g) is added to a solution composed of90 mL water with 10 mg (0.065 mmol) TEMPO and 0.22 g (2 mmol) sodiumbromide. Hydrogen peroxide 3% is added (0.9 mL, 1 mmol) and the reactionstirred at RT for 10 minutes to 2 hours. The material is washed withwater, dried, and used without further modification in the following ZnOdeposition step.

Example 6 Immobilization of Nanoparticles on a Phosphorylated orCarboxylated Cellulose Surface

Ca. 1 mg/mL nanoparticles are suspended in water, ethyl alcohol, orother solvent. The phosphorylated or carboxylated cellulose textile isadded to the suspension and the suspension is gently mixed over areaction period of 1 to 12 hours. The textile is removed from thesuspension and subjected to tumble drying or another drying procedure toforce surface condensation and cure remaining groups.

The following example discloses modifying UV-blocking nanoparticles witha self-assembled monolayer (SAM) or polymer layer containing an activechemical group capable of binding to the fabric and deposited on thefabric from solution.

Example 7 Grafting to Attachment of Cellulose to Nanoparticles ThroughReactive Groups

In this method, ZnO particles are synthesized separately by any of themeans discussed in Examples 1-3 or the ZnO particles may be purchasedcommercially. The ZnO particles are suspended in water or a weaknon-nucleophilic aqueous buffer and an organosilane or phosphonate withone of the given combinations of reactive groups, as shown in Table 1,is added. Multidentate ligand or polymeric silanes may also be added tothis mixture to facilitate the formation of a durable reactive layer andan oxide, alkoxide, or salt of another metal such as Ti or Si may beadded first to form a surface layer of another oxide in the ZnOparticles. After a reaction time of 1 to 12 hours, the particles arecollected by centrifugation and washed with water. The particles arethen resuspended in water or buffer and added to the textile. Theconditions for binding of the particles to the textile vary depending onthe headgroup, as shown in Table 1, but may involve direct applicationof the particles to the textile similarly to the process disclosed inExample 6, raising the pH of the suspension containing the textile, orheating the textile either in or after removal from the suspension. Thisprocess has the advantage of yielding extremely fine control over thenature of the linkage between particle and textile. This process has afurther advantage in that the treated textile will be durable due to therobustness of self-assembled siloxane layers on oxide.

TABLE 1 Molecule name Commer- (if commercially cially available) LinkerHeadgroup available? 3-glycidoxypropyl- Triethoxysilane Glycidyl etherYes triethoxysilane 2-(3,4- Triethoxysilane Cyclohexyl Yescyclohexyloxy) oxide ethyltriethoxysilane Hydroxymethyl- TriethoxysilaneHydroxymethyl Yes triethoxysilane Isocyanatopropyl TrimethoxysilaneIsocyanate Yes trimethoxysilane Bis(triethoxysilyl) Triethoxysilane N/AYes ethane (2) 6-azidosulfonylhexyl Triethoxysilane Axidosulfonyl Yestriethoxysilane Triethoxysilane Vinylsulfone No Triethoxysilane Arylazide No Phosphonate Glycidyl ether No Phosphonate Cyclohexyl No oxidePhosphonate Azidosulfonyl No Phosphonate Vinylsulfone No PhosphonateAryl azide No Bis(triethoxysilyl) Triethoxysilane Secondary Yespropylamine (2) amine APTES/EGDE Triethoxysilane Amine/Ethyl- Yes, 2 eneglycol components diglycidyl ether

The terms “fabric” or “textile” are intended to include fibers,filaments, yarn, melt, textiles, material, woven and non-woven fabric,knits, and finished products such as garments. The methods describedherein may be used in treating fibers, filaments, yarn, textiles, andfabrics. For example, fibers may be initially treated by use of one ormore of the disclosed methods and the fibers may be manufactured into afabric or a textile. Once manufactured into a fabric, the fabric may betreated by use of one or more of the disclosed methods. In this manner,individual fibers and the entire fabric are treated to incorporate UVprotection. As can be appreciated, the treated fabric may be used tomanufacture a garment such as, by way of example only, shirts, pants,hats, coats, jackets, shoes, socks, uniforms, athletic clothing, andswimwear. It is also possible and contemplated that the treated fabricmay be used to construct non-apparel items such as blankets, sheets,sleeping bags, backpacks, and tents.

Further, it is also possible to further modify ZnO particles with a thinlayer of other oxides in a “core-shell” type procedure by adding areactive precursor to a suspension of the ZnO oxides. Oxides that can bedeposited in this manner include SiO₂ from tetraethoxysilane (TEOS) orsodium silicate, and Al₂O₃ and TiO₂ either from the appropriatealkoxides, aluminate/titanate compounds, or other hydrolyzable aluminumor titanium compounds. A second oxide shell of this type may enhance theformation and stability of both directly applied ZnO-textile conjugatesand those formed by modification of nanoparticles with an organicmonolayer. ZnO can also be modified by the addition of a multidentatesilane along with a silane containing the desired functional group. Themultidentate silane yields a more densely crosslinked siloxane surfacethan monodentate silanes alone, forming a more stable layer on ZnO.

Although the above examples and methods are applicable to themanufacturing process in which ultraviolet radiation protection isincorporated into the fabric, textile, or garment when initiallyproduced, the following discloses various methods of incorporatingultraviolet radiation protection directly to clothing being laundered.By use of the following methods, a garment after purchase may be made aprotected garment by an end user.

In general, the methods may comprise the self-assembly of certainpolyanionic materials onto a ZnO surface to create a linker which willbind the particles to a cellulose (cotton) surface. Several acidic oroxyanion functional groups are capable of self-assembly onto ZnO. Thesefunctional groups include siloxane, silanol, carboxylic acid,carboxylate, phosphonic acid, phosphonate, boronic acid or other groupscapable of binding to oxide layers. Boronic acid is capable of formingvery strong interactions with carbohydrates, including theglycosidically linked glucose units making up cellulose. One method orapproach is to prepare a polymer bearing boronic acid groups and usethat polymer to bind ZnO to cotton.

Various methods or processes are disclosed herein for the treatment offabric to incorporate UV protection in the fabric by use of a laundryadditive. One method is identified as the cellulose-to-oxide method. Asecond method is termed the oxide-to-cellulose method. A third method isdescribed as the free mixing method.

Example 8 the Cellulose-to-Oxide Method

In this method, cotton garments are pre-treated with boronic acidpolymer resulting in cloth or fabric coated with boronic acid groupscapable of binding to suspended uncoated ZnO particles. A home washingmachine having the capability of adding a substance on a delayed basismay be used. In particular, boronic acid polymer is added to laundrydetergent or added at the beginning of the laundry cycle. A suspensionof ZnO particles may be added to a compartment in the washing machinethat will dispense the particles on a delayed basis. For example,several washing machines have a compartment for storing bleach which isdispensed later on in the laundry cycle. The suspension of ZnO particlesmay be placed in the bleach compartment to be dispensed at the time thatbleach would normally be dispensed into the washing machine. The washingmachine would initially mix the clothing with the boronic acid material.This will result in the clothing bearing boronate groups. At the end ofthe delayed period the washing machine will dispense the suspension ofZnO particles into the washing machine. The ZnO particles will bind tothe boronate groups and become attached to the clothing. It is alsopossible and contemplated that the suspension of ZnO particles may bemanually added to the washing machine in a delayed manner. Manuallyadding the suspension may be required if the washing machine is notequipped with a compartment for adding bleach on a delayed basis.

Example 9 Oxide-to-Cellulose Method

In this method, ZnO particles are treated with boronic acid polymer.Once prepared, these particles may be either mixed with laundrydetergent and distributed in that form or sold as a separate additivethat may be added to laundry detergent. The particles mixed with thelaundry detergent or the separate additive is used in the washingmachine as normal. During the course of the wash cycle, the boronic acidgroups attach to the ZnO particles would assemble on and bind to cottonor other cellulose clothing. This results in an ultraviolet protectedgarment.

Example 10 Free Mixing Method

In this method, boronic acid polymer and ZnO particles (untreated) areincorporated into the laundry detergent preparation in the solid phase.When added to a laundry cycle or wash cycle the detergent and water willsolubilize these materials causing boronic acid polymer to assemble onboth ZnO and cellulose. This will result in linked ZnO material. Thismethod may require more boronic acid polymer and ZnO particles then themore controlled methods disclosed in Examples 8 and 9 to yield adequategrafting densities of ZnO on clothing.

Use of any of the methods disclosed in Examples 8, 9, or 10 will resultin ZnO particles being bound to the fabric that is being washed in aconventional household washing machine. Once the ZnO particles are boundto the fabric, the fabric will have incorporated therein ultravioletradiation protection. It is also possible and contemplated that thevarious methods described in Examples 8, 9, and 10 may be used more thanonce to incorporate ultraviolet radiation protection into clothing. Forexample, clothing may be treated by use of one or more of these methodsand over time and after numerous washings the ultraviolet radiationprotection may diminish. If there is any concern about the ultravioletradiation protection of the garment, the garment may be washed using thevarious methods discussed in Examples 8, 9, and 10. Further, it ispossible that a consumer may purchase a garment that has been treatedusing the methods described in Examples 1-7. Again, over time theultraviolet radiation protection of the garment may decline. Theconsumer may use the methods disclosed in Example 8, 9, and 10 to washthe garment to again incorporate ultraviolet radiation protection intothe garment.

All synthetic material such as polyester and nylon that is used in themanufacture of athletic clothing or active wear clothing may be renderedUV-absorbing using a ZnO preparation. These types of fabrics may resisttreatment using the methods as outlined with respect to Examples 8, 9,and 10. One solution to this problem is to prepare ZnO particles coatedwith functional groups capable of being grafted directly to polyester ornylon materials. This may be accomplished by using benzophenonephotografting chemistry. The following examples and methods areapplicable to the manufacturing process in which ultraviolet radiationprotection is incorporated into the artificial or synthetic composition,polymer, fabric, textile, or garment when initially produced.

The following methods provide for the direct grafting of ZnO particlesto nonpolar, non-natural polymers such as nylon and polyester. Nylon andpolyester have little in the way of chemical functionality, containingonly aliphatic and aromatic C—H bonds and amide or ester linkagesbetween monomers. The method is capable of directly functionalizing C—Hbonds. The following method describes preparing ZnO particles coatedwith functional groups capable of being grafted directly to polyester ornylon materials by using the photografting reaction of benzophenone.

Example 11 Grafting ZnO onto Artificial or Synthetic Fibers

In this method, an artificial fabric composed of polyester, nylon, orother polymer lacking hydroxyl functional group is modified by use of apreparation of a zinc oxide particle modified with a layer of reactivegroups capable of C—H activation. Examples of the reactive functionalgroup capable of C—H activation are benzophenone, sulfonylazides, arylazides, or diazonium salts. The prepared particles are coated onto thefabric and a reaction is initiated using UV light, heat, or both. By wayof example only, a mercury-vapor UV lamp may be used and the time forexposure may be one hour. Unbound particles are washed off the fabric.This second step, a curing step, bonds the prepared particles to thefabric. This method adds a second UV-absorbing chromophore whichcross-links and becomes further bonded to the polymer surface of thefabric upon exposure to UV light. In this method, zinc oxide particlescan be composed of pure zinc oxide or zinc oxide coated with aluminum,titanium, or silicon oxides in a core-shell configuration. The result isan artificial fabric with photografted zinc oxide particles.

By way of example, the zinc oxide particles were prepared in thefollowing manner. Five grams of zinc oxide nanoparticles were used andsuspended in a solution of 98% ethyl alcohol. Two grams of benzophenonesilane linker were suspended in this solution and the pH of the solutionwas adjusted to 12. After twelve hours, the zinc oxide particles wererecovered by centrifugation and dried overnight at 50-60° C. in an oven.

It is also possible to prepare a phosphoether of 4-hydroxybenzophenoneand use this self-assembling molecule to functionalize ZnO particles.The resulting particles, having a monolayer of nonpolar molecules, willbe substantially nonpolar and will adhere to nonpolar polyester andnylon. In order to bond the particles to the polymer surface an UV lightmay be used to initiate a reaction. Again, the process has the advantageof adding a second UV absorbing chromophore which cross-links andbecomes further bonded to the polymer surface upon exposure to UV light.

The following describes an additive for incorporating UV protection intoa polymer prior to the polymer being placed into a spinneret or prior tothe polymer being formed into fibers. Nylon and polyester have little inthe way of chemical functionality, containing only aliphatic andaromatic C—H bonds and amide or ester linkages between monomers. Theadditive is capable of directly functionalizing C—H bonds.

Example 12 Additive

An artificial fabric composed of polyester, nylon, or other polymerlacking hydroxyl functional group is modified by use of an additive of aquantity of zinc oxide particles modified with a layer of a reactivegroup that forms a bond with a synthetic polymer having C—H bonds.Examples of the reactive functional group capable of C—H activation arebenzophenone, sulfonylazides, aryl azides, diazonium salts, isocyanate,oxime, and azo. The prepared particles may be added to the syntheticpolymer prior to the synthetic polymer being placed into a spinneret.Further, it is also contemplated that the additive may be packaged withthe synthetic polymer and the packaged additive and synthetic polymermay be placed into the spinneret. The modified zinc oxide particles canalso be coated with aluminum, titanium, or silicon oxides in acore-shell configuration.

By way of example, the zinc oxide particles were prepared in thefollowing manner. a quantity of zinc oxide particles was suspended in asolution of 98% ethyl alcohol, a quantity of benzophenone silane linkerwas suspended in the solution of zinc oxide particles and 98% ethylalcohol, the pH of the solution of zinc oxide particles, 98% ethylalcohol, and benzophenone silane linker was adjusted to 12, the pHadjusted solution of zinc oxide particles, 98% ethyl alcohol, andbenzophenone silane linker was placed into a centrifuge, the zinc oxideparticles prepared by centrifugation was recovered after a period oftime, and the recovered prepared zinc oxide particles were dried. Byfurther way of example only, five grams of zinc oxide nanoparticles wereused and suspended in a solution of 98% ethyl alcohol. Two grams ofbenzophenone silane linker were suspended in this solution and the pH ofthe solution was adjusted to 12. After twelve hours, the zinc oxideparticles were recovered by centrifugation and dried overnight or foreight hours at 50-60° C. in an oven.

By way of example only and in not a limiting sense, it is also possibleto prepare a phosphoether of 4-hydroxybenzophenone and use thisself-assembling molecule to functionalize ZnO particles. The resultingparticles, having a monolayer of nonpolar molecules, will besubstantially nonpolar and will adhere to nonpolar polyester or nylon.The resulting or modified zinc oxide particles can also be coated withaluminum, titanium, or silicon oxides in a core-shell configuration.Further, it is to be understood that many other benzophenone derivativesare suitable for use to prepare a self-assembling molecule tofunctionalize ZnO particles.

Synthetic material such as rayon that is used in the manufacture ofathletic clothing or active wear clothing may be rendered UV-absorbingand antimicrobial using a ZnO preparation. This type of fabric mayresist treatment using the methods as outlined with respect to Examples8, 9, and 10. One solution to this problem is to prepare ZnO particlescoated with functional groups capable of being grafted directly to rayonmaterial. This may be accomplished by using benzophenone photograftingchemistry. The following examples and methods are applicable to themanufacturing process in which ultraviolet radiation protection andantimicrobial protection are incorporated into the rayon polymer,fabric, textile, or garment when initially produced.

The following methods provide for the direct grafting of ZnO particlesto rayon. The following method describes preparing ZnO particles coatedwith functional groups capable of being grafted directly to rayonmaterial by using the photografting reaction of benzophenone.

Most commercial rayon production utilizes the viscose process. Thisprocess may comprise the following steps. Initially, purified celluloseis provided from specially processed wood pulp to form cellulose sheets.The cellulose sheets are saturated with a solution of caustic soda orsodium hydroxide. The solution is allowed to steep for enough time sothat the caustic solution penetrates the cellulose to convert some of itinto soda cellulose, the sodium salt of cellulose. This is known as thesteeping step. This is necessary to facilitate controlled oxidation ofthe cellulose chains and the ensuing reaction to form cellulosexanthate. The soda cellulose is squeezed mechanically to remove anyexcess caustic soda solution. This is known as the pressing step. Thesoda cellulose is mechanically shredded to increase surface area and tomake the cellulose easier for further processing. This is known as theshredding step. This shredded cellulose is sometimes referred to as“white crumb”. White crumb is then allowed to stay in contact withambient air so that an oxidation process occurs. The high alkalinity ofthe white crumb partially oxidizes the cellulose to degrade thecellulose to lower molecular weights. Degradation of the cellulose mustbe carefully controlled in order to produce chain lengths short enoughto provide manageable viscosities in the spinning solution. However, thechain lengths must be long enough to provide good physical properties tothe fiber product. This is known as the aging step. Once the white crumbis properly aged the white crumb is placed in a churn or other mixingvessel. Once in the churn the white crumb is treated with gaseous carbondisulfide. The soda cellulose reacts with the carbon disulfide to formxanthate ester groups. The carbon disulfide also reacts with thealkaline medium to form inorganic impurities which give the cellulosemixture a yellow color and this material is called “yellow crumb”. Theyellow crumb is a block copolymer of cellulose and cellulose xanthatebecause accessibility to the carbon disulfide is restricted in thecrystalline regions of the soda cellulose. This is known as thexanthation step. In a next step, known as the dissolving step, theyellow crumb is dissolved in aqueous caustic solution. The largexanthate substituents on the cellulose force the chains apart, reducingthe interchain hydrogen bonds and allowing water molecules to solvateand separate the chains. This leads to a solution of insolublecellulose. The yellow crumb is not completely soluble at this stage dueto the blocks of un-xanthated cellulose in the crystalline regions. Thecellulose xanthate solution or suspension has a very high viscosity. Theviscose is allowed to stand for a period of time to ripen. This is knownas the ripening step. In a next step, the filtering step, the viscose isfiltered to remove undissolved materials that might disrupt the spinningprocess or cause defects in the rayon filament. The very next step inthe process is known as the degassing step. In the degassing stepbubbles of air trapped in the viscose are removed. After the degassingstep is a step known as the spinning or wet spinning step. Prior to thespinning step an additive, as disclosed further herein, is introduced.In the spinning step the viscose is forced through a spinneret. Thespinneret has a number of small holes and each hole produces a finefilament of viscose. The result of the spinning step is the formation offine filaments of rayon having ultraviolet radiation protection andantimicrobial protection incorporated therein. In the next step, knownas the drawing step, the rayon filaments are stretched while thecellulose chains are still relatively mobile. The rayon filaments arewashed to remove any salts or other water soluble impurities. This isthe washing step of the process. Finally, the rayon may be passedthrough a rotary cutter to provide a fiber which can be processed inmuch the same way as cotton. This is the cutting step. As can beappreciated, when the quantity of rayon is treated or incorporated withthe additive, as discussed herein, the rayon has the properties ofultraviolet radiation protection and antimicrobial protection.

The following describes an additive for incorporating UV protection andantimicrobial protection into rayon prior to the wet spinning step, orprior to rayon being placed into a spinneret, or prior to rayon beingformed into fibers. Rayon has little in the way of chemicalfunctionality, containing only aliphatic and aromatic C—H bonds andamide or ester linkages between monomers. The additive is capable ofdirectly functionalizing C—H bonds.

Example 13 Additive

An artificial fabric composed of rayon is modified by use of an additiveof a quantity of zinc oxide particles modified with a layer of areactive group that forms a bond with rayon having C—H bonds. Examplesof the reactive functional group capable of C—H activation arebenzophenone, sulfonylazides, aryl azides, diazonium salts, isocyanate,oxime, and azo. The prepared particles may be added to the rayon priorto the rayon being placed into a spinneret or prior to a wet spinningstep. Further, it is also contemplated that the additive may be packagedwith rayon and the packaged additive and rayon may be placed into thespinneret. The modified zinc oxide particles can also be coated withaluminum, titanium, or silicon oxides in a core-shell configuration.

By way of example, the zinc oxide particles were prepared in thefollowing manner. A quantity of zinc oxide particles was suspended in asolution of 98% ethyl alcohol, a quantity of benzophenone silane linkerwas suspended in the solution of zinc oxide particles and 98% ethylalcohol, the pH of the solution of zinc oxide particles, 98% ethylalcohol, and benzophenone silane linker was adjusted to 12, the pHadjusted solution of zinc oxide particles, 98% ethyl alcohol, andbenzophenone silane linker was placed into a centrifuge, the zinc oxideparticles prepared by centrifugation was recovered after a period oftime, and the recovered prepared zinc oxide particles were dried. Byfurther way of example only, five grams of zinc oxide nanoparticles wereused and suspended in a solution of 98% ethyl alcohol. Two grams ofbenzophenone silane linker were suspended in this solution and the pH ofthe solution was adjusted to 12. After twelve hours, the zinc oxideparticles were recovered by centrifugation and dried overnight or foreight hours at 50-60° C. in an oven.

By way of example only and in not a limiting sense, it is also possibleto prepare a phosphoether of 4-hydroxybenzophenone and use thisself-assembling molecule to functionalize ZnO particles. The resultingparticles, having a monolayer of nonpolar molecules, will besubstantially nonpolar and will adhere to rayon. The resulting ormodified zinc oxide particles can also be coated with aluminum,titanium, or silicon oxides in a core-shell configuration. Further, itis to be understood that many other benzophenone derivatives aresuitable for use to prepare a self-assembling molecule to functionalizeZnO particles.

From all that has been said, it will be clear that there has thus beenshown and described herein a product for incorporating ultravioletradiation protection and antimicrobial protection into rayon whichfulfills the various advantages sought therefore. It will becomeapparent to those skilled in the art, however, that many changes,modifications, variations, and other uses and applications of thesubject product for incorporating ultraviolet radiation protection andantimicrobial protection into rayon are possible and contemplated. Allchanges, modifications, variations, and other uses and applicationswhich do not depart from the spirit and scope of the disclosure aredeemed to be covered by the disclosure, which is limited only by theclaims which follow.

What is claimed is:
 1. A product having ultraviolet radiation protectionand antimicrobial protection comprising: a quantity of rayon; a quantityof zinc oxide particles with each particle having a surface; and aquantity of a reactive group for modifying each surface of each zincoxide particle, the quantity of the reactive group for incorporating thequantity of zinc oxide particles into the quantity of rayon prior to thequantity of rayon being formed into a fiber.
 2. The product of claim 1wherein the reactive group is benzophenone.
 3. The product of claim 1wherein the reactive group is sulfonylazides.
 4. The product of claim 1wherein the reactive group is aryl azides.
 5. The product of claim 1wherein the reactive group is diazonium salts.
 6. The product of claim 1wherein the zinc oxide particles are coated with aluminum.
 7. Theproduct of claim 1 wherein the zinc oxide particles are coated withtitanium.
 8. The product of claim 1 wherein the quantity of rayon, thequantity of zinc oxide particles, and the quantity of the reactive groupare packaged together in a package.
 9. A product for incorporatingultraviolet radiation protection and antimicrobial protection into rayonprior to the rayon being formed by use of a spinneret comprising: aquantity of rayon; a quantity of zinc oxide particles; and a quantity ofa phosphoether of 4-hydroxybenzophenone.
 10. The product of claim 9wherein the zinc oxide particles are coated with aluminum.
 11. Theproduct of claim 9 wherein the quantity of rayon, the quantity of zincoxide particles, and the quantity of phosphoether of4-hydroxybenzophenone are packaged together in a package.
 12. Theproduct of claim 9 wherein the zinc oxide particles are coated withsilicon oxides.
 13. The product of claim 9 wherein the zinc oxideparticles are coated with titanium.
 14. The product of claim 9 whereinthe zinc oxide particles are coated with aluminum.
 15. A product forincorporating ultraviolet radiation protection and antimicrobialprotection into rayon prior to forming rayon comprising: a quantity ofrayon; and a quantity of prepared zinc oxide particles modified with alayer of a reactive group that forms a bond with the quantity of rayonwith the quantity of prepared zinc oxide particles prepared bysuspending a quantity of zinc oxide particles in a solution of 98% ethylalcohol, suspending a quantity of benzophenone silane linker in thesolution of zinc oxide particles and 98% ethyl alcohol, adjusting the pHof the solution of zinc oxide particles, 98% ethyl alcohol, andbenzophenone silane linker to 12, placing the pH adjusted solution ofzinc oxide particles, 98% ethyl alcohol, and benzophenone silane linkerinto a centrifuge, recovering the zinc oxide particles prepared bycentrifugation after a period of time, and drying the recovered preparedzinc oxide particles for a period of time.
 16. The product of claim 15wherein the quantity of benzophenone silane linker is two grams.
 17. Theproduct of claim 15 wherein the time that the recovered prepared zincoxide particles are dried is eight hours.
 18. The product of claim 15wherein the recovered prepared zinc oxide particles are dried in anoven.
 19. The product of claim 15 wherein the recovered prepared zincoxide particles are dried in an oven set at 50-60° C.
 20. The product ofclaim 15 wherein the quantity of rayon and the quantity of prepared zincoxide particles are packaged together in a package.